1. High brightness, coating up to the mirror level, comparable with the bright acid zinc.

2. High plating capacity, very uniform coating thickness, high current area (4A / dm2) and low current area (0.2A / dm2) coating thickness ratio of 1.2-1.4 (general products 2.0-3.0), significant savings in zinc Consumption, while saving costs.

3. Good flexibility, coating 20um can be bent at 200 ℃ constant temperature baking 60 minutes immediately after immersion in cold water quenching, coating does not blister.

4. Deep plating ability, better than cyanide zinc and zinc.

5. Bath composition, temperature, electricity and other management of a wide range of easy management.

6. Easy to use hexavalent chromium-free passivation passivation, can be stable corrosion resistance.